Ceramic Zro2 Zirconium Oxide Zirconia Ceramic Rings for Wire Drawing Capstan

• Standard: Standard
• Coating: Uncoated
• Material: Ceramics
• Model NO.: Zirconia ceramic ring
• Processing Service: Bending, Welding, Cutting, Punching, Decoiling, Mo
• Applicable Industries: Industry
• Finished: Polish
• Color: White
• Transport Package: Plastic Bag, Wooden Box
• Specification: 0.1mm,0.2mm,0.5mm,1.0mm or according to requiement
• Trademark: yinghua
• Origin: China
• Package Size: 20.00cm * 20.00cm * 20.00cm
• Package Gross Weight: 1.000kg

Product Description

TZP ceramic blade is made from Yttria partially stabilized zirconia, Possessed with extreme sharpness and hardness, superior resistance to corrosion and abrasion, low friction coefficient make zirconia ceramic particularly effective in slitting operations, And blade life can be more than 100 times that of conventional steel blade which greatly decrease the frequeny and time of blade replacement, also these properties ensure the precision cut and better looking edges. All the characteristics of Zirconia make it an attractive material in many applications include:
1. Superb Corrosion Resistance;
2. Antimagnetic;
3. High Electrical Insulation Properties;
4. High-shock Applications.
At present, it is mainly used in food processing industry, textile industry, rubber and plastic cutting, automobile manufacturing industry and medical field.

Item		Unit	99 Al2O3	ZrO2
Physical Characteristics	Bulk density	g/cm3	3.9	6.05
	Water absorption	%	0	0
Mechanical Characteristics	Flexural strength	Mpa	360	1000
	Hardness Vickers	Gpa	15.6	89
	Elastic modulus	Gpa	370	200
	Poisson's ratio	-	0.23	0.31
Thermal Characteristics	Linear expansion coefficient	(20-5000°C) 10-6/0°C	8	10
	Thermal conductivity	w/(m·k)	32	2.5
	Specific Heat	×10-3J/(kg·K)	0.9	0.5
Electrical Characteristics	Dielectric constant (1MHZ	-	9.9	N.A.
	Dielectric loss angle	×10-4	1	N.A.
	Dielectric strength	×10-6V/m	15	N.A.