| Application: | Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic |
|---|---|
| Type: | Ceramic Parts |
| Size: | Customized |
|
Still deciding? Get samples of US$ 10/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Magnesium oxide partially stabilized zirconia ceramics (Mg-PSZ or MSZ) have unparalleled advantages in high temperature and high humidity, and can be used for a long time without aging at low temperature. High quality Mg-PSZ ceramics have good moisture resistance, thermal shock resistance, excellent fracture toughness and high temperature mechanical strength, can withstand use temperature up to 800 ºC or higher (up to 2000 ºC), Mg-PSZ ceramics is free from wetting and best corrosion resistance to acid, alkali, liquid glass and molten metal .
| ITEM | 1 | 2 | ||||
| Y-TZP | MgO-PSZ | |||||
| 1 | (%) | ZrO2 | Y2O3 | ZrO2 | MgO | |
| Chemical Composition | 94.6 | 5.2 | 96.5 | 3.5 | ||
| 2 | White | Yellow | ||||
| Color | ||||||
| 3 | (g/cm3) | 6.05 | 5.70 | |||
| Density | ||||||
| 4 | (%) | 0 | 0 | |||
| Water Absorption | ||||||
| 5 | 9 | 9 | ||||
| Hardness Mohs | ||||||
| 6 | (Kg/mm2) | 1300 | 1100 | |||
| Hardness Vickers | ||||||
| 7 | (Gpa) | 200 | 250 | |||
| Young's Modulus | ||||||
| 8 | (MPa) | 1250 | 450 | |||
| Bending Strength | ||||||
| 9 | (Mpa*M1/3) | 10.0 | 6.5 | |||
| Fracture Toughness | ||||||
| 10 | (MPa) | 3000 | 2500 | |||
| Compressive Strength | ||||||
| 11 | (10-6/K) | 10.0 | 10.0 | |||
| Expansion Coefficient | ||||||
| 12 | (W/mK) | 3 | 3 | |||
| Thermal Conductivity | ||||||
| 13 | 20.0 | 28.0 | ||||
| Dielectric Constant | ||||||
| 14 | (Ω·Cm) | >1012 | >1014 | |||
| Volume Resistivity | ||||||