| Application: | Refractory |
|---|---|
| Type: | Ceramic Parts |
| Feature: | High Hardness, Good Wear Resistance, High Toughnes |
|
Still deciding? Get samples of US$ 10/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Our glass-ceramics offer exceptional processing properties, allowing for milling, planing, grinding, drilling, sawing, and tapping with standard metal tools and equipment. Unlike traditional insulating materials, our glass-ceramics can achieve high precision and complex shapes similar to cast iron.
With meticulous machining methods and accurate cutting parameters, our glass-ceramics can achieve tolerance grades as tight as IT7 and a finish of 0.5 μm. Machining accuracy of 0.005mm is easily attainable, making it ideal for applications in automotive, military, aerospace, medical equipment, and more.
Our glass-ceramic ceramics are perfect for thin-walled coil skeletons, insulation supports, and precision instruments due to their superior strength, low gas rate, temperature resistance, and durability. They outperform materials like boron nitride, PTFE, and alumina porcelain, offering excellent thermal shock resistance from 800 ºC to 0 ºC.
Experience the benefits of our machinable ceramics in aviation, aerospace, electronic substrates, high-temperature insulation, ion plating, vacuum coating, and medical equipment. Accelerate your engineering progress and save on research and development costs with our innovative glass-ceramics.
| Glass Ceramics Properties | |||
| Color | White | Density | 2.7g/cm3 |
| Compressive Strength | 488MPa | Bending Strength | 108MPa |
| Thermal Conductivity | 1.68 W/m.K | Thermal expansion coefficient | 8.6×10-6 K-1 |
| Application Tem(Max) | 800ºC | Volume resistivity | 1014Ω.cm |
| Dielectric constant | 6.5@1Hz | Hardness(HRC) | 40 |