25ml 30ml 50ml Pure 99.99 Zirconium Oxide Crucible

• Standard: Standard
• Coating: Uncoated
• Material: Ceramics
• Model NO.: Oxide Crucible
• Processing Service: Bending, Welding, Cutting, Punching, Decoiling, Mo
• Applicable Industries: Industry
• Finished: Polish
• Color: White
• Transport Package: Plastic Bag, Wooden Box
• Specification: 0.1mm,0.2mm,0.5mm,1.0mm or according to requiement
• Trademark: yinghua
• Origin: China
• Package Size: 20.00cm * 20.00cm * 20.00cm
• Package Gross Weight: 1.000kg

Product Description

TZP ceramic blade is made from Yttria partially stabilized zirconia, Possessed with extreme sharpness and hardness, superior resistance to corrosion and abrasion, low friction coefficient make zirconia ceramic particularly effective in slitting operations, And blade life can be more than 100 times that of conventional steel blade which greatly decrease the frequeny and time of blade replacement, also these properties ensure the precision cut and better looking edges. All the characteristics of Zirconia make it an attractive material in many applications include:
1. Superb Corrosion Resistance;
2. Antimagnetic;
3. High Electrical Insulation Properties;
4. High-shock Applications.
At present, it is mainly used in food processing industry, textile industry, rubber and plastic cutting, automobile manufacturing industry and medical field.

Density, ρ	g/cm3	6.04
Water Absorption	% @ room temperature (R.T.)	0
Hardness	Mohs	6.5
Hardness	Knoop (kg/mm2)	1600
Compressive Strength	MPa @ R.T.	2500
Fracture Toughness, KIc	MPa x m1/2	13
Max. Use Temperature (in air)	ºC	500
Thermal Shock Resistance	T (ºC)	280-360
Thermal Conductivity	W/m-K @ R.T.	2.7
Coefficient of Linear Thermal Expansion, αl	µm/m-ºC  (~25ºC through ±1000ºC)	11
Dielectric Constant 1 MHz @ R.T. ASTM D150 26 @ 100kHz	1 MHz @ R.T.	26 @ 100kHz
Dielectric Strength	kV/mm	9
Electrical Resistivity	cm @ R.T.	>104