Aluminum Nitride Aln Ceramic Sheet Substrate

• Application: Electronic Ceramics
• Type: Ceramic Rings
• Thermal Conductivity: 180~190
• Model NO.: Ceramic Sheet Substrate
• Size: Customized
• Advantage: Long Service Life
• Color: White
• Applicable Industries: Industry
• Material: Aluminun Nitride Ceramics
• Transport Package: Foam Package
• Specification: L0.5~200MM*W0.5~200MM*T0.1~2MM
• Trademark: YinghuaMT
• Origin: China
• Production Capacity: 50000
• Package Size: 20.00cm * 20.00cm * 20.00cm
• Package Gross Weight: 1.000kg

Product Description

Aluminum Nitride Ceramics are ceramics with aluminum nitride (AIN) as the main crystal phase.
AlN crystals use [AIN4] tetrahedrons as the structural unit covalent bond compounds, with a wurtzite structure, belonging to the hexagonal system. Chemical composition: AI 65.81%, N 34.19%, specific gravity 3.261g/cm3, white or off-white, single crystal is colorless and transparent, the sublimation decomposition temperature under normal pressure is 2450°C. A high-temperature heat-resistant material. Thermal expansion coefficient (4.0-6.0)X10-6/°C. Polycrystalline AIN thermal conductivity of 260W / (m.k), 5-8 times higher than aluminum oxide, so the heat and shock resistance, can withstand extremely hot 2200 °C. In addition, aluminum nitride has the property of being free from attack by molten aluminum and other molten metals and g allium arsenide, and particularly has excellent corrosion resistance to molten aluminum liquid.
application
1. Aluminum nitride powder has high purity, small particle size and large activity, and is the main raw material for manufacturing high thermal conductivity aluminum nitride ceramic substrates.
2. Aluminum nitride ceramic substrate has high thermal conductivity, low coefficient of expansion, high strength, high temperature resistance, chemical resistance, high resistivity and low dielectric loss. It is an ideal large-scale integrated circuit heat-dissipating substrate and packaging material.
3, aluminum nitride high hardness, more than traditional alumina, is a new type of wear-resistant ceramic materials, but due to high cost, can only be used for serious wear and tear.
4. Using AIN ceramics for heat resistance, melt erosion and thermal shock resistance, GaAs crystal crucibles, Al evaporating dishes, magnetic fluid power generation devices, and high-temperature turbine corrosion resistance components can be fabricated, and their optical properties can be used as infrared windows. Aluminum nitride films can be made into high-frequency piezoelectric elements, VLSI substrates, etc.
5, aluminum nitride heat, corrosion resistance to molten metal, acid stability, but easily eroded in alkaline solution. The exposure of AIN's neonatal surface to moist air will generate a very thin oxide film. Using this feature, it can be used as a crucible and cast mold material for metal smelting of aluminum, copper, silver, lead, and the like. AIN ceramics have good metallization properties and can be used as a substitute for toxic oxidized enamels in the electronics industry.

Application:
1. Application of optical communication devices

2. Special refrigeration unit

3.LED industry

4. Automotive electronic module

5. High efficiency power module

6. High frequency microwave application

7. Power electronic components

Material's mechanical properties and thermal conductivity dielectric properties. 

PROPERTY	ITEMS	UNIT	ALN
Physical	Color	-	Grey
	Water absorption	%	0
	Reflectivity	%	30*
Electrical	Dielectric Constant (1MHz)	-	8~10
	Dielectric Loss	*10^-4	3
	Dielectric strength	MV/m or KV/mm	>17
	Insulation/Volume resistance	Ω·cm	>10^14
Mechanical	Density after sintering (Bulk density)	g/cm3	3.26
	Flexural Strength (3 point)	Mpa	~380
	Hardness		9.3
	Elasticity (Young's Modulus)	GPa	302
	Surface Roughness	μm	0.3~0.6
	Camber	Lenght%	≤2
Thermal	Coefficient of Thermal Expansion (CTE)	ppm/°C	2~3
	Coefficient of Thermal Expansion (CTE) RT~500 °C	ppm/°C	2.5~3.5
	Thermal Conductivity (25°C)	W/m K	170