High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling

Product Details
Application: Industrial Ceramic
Type: Ceramic Balls
Size: OEM
Still deciding? Get samples of $ !
Request Sample
Gold Member Since 2018

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

Number of Employees
3
Year of Establishment
2015-12-28
  • High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling
  • High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling
  • High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling
  • High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling
  • High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling
  • High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling
Find Similar Products

Basic Info.

Model NO.
bead
Advantage
Long Service Life
Color
White
Applicable Industries
Hotels, Garment Shops, Building Material Shops
Material
Zirconia Ceramic
Transport Package
Plastic Bag, Wooden Box
Specification
0.1MM~50MM
Trademark
yinghua
Origin
China

Product Description


1. Introduction:
TZP Milling Media is made from Yttria partially stabilized zirconia, and available for any kinds of mills such as micro mill, ultromicro mill, vibratory mill and ball mill to grind and disperse the material effectively and economically. Characterized with high density and toughness, super hardness, excellent Wear and corrosion resistance, the TZP milling media is regarded as an most attractive material in many applications include: electronic slurry, ceramic powder, magnetic material, battery material, rare-earth material, nonmetal ore, painting, dye, ink, calcium, titanium, pesticide, food stuff and medicine etc. Superior grinding efficiency and minimizing product contamination from media wear are most valued.
2. Main Properties:
Type-1: High Density
Constituents (%) ZrO2
Y2O3
94.6
5.25
Density g/cm³ 6.05
Open Porosity % 0
Hardness Vickers Hv 1250
E modulus Gpa 200
Bending strength (4-point) MPa 1300
Fracture strength MPa*m1/2 8
CTE(20~4000C) *10-6/ K 9.6

Type-2: Low Density
Constituents (%) ZrO2
Y2O3
94.6
5.25
Density g/cm³ 5.80
Hardness Vickers Hv 1100
E modulus Gpa 200
Bending strength (4-point) MPa 900
Fracture strength MPa*m1/2 >6
3. Main Specifications:
Ball: OD0.6mm, OD0.8mm, OD1.0mm, OD1.2mm, OD1.4mm, OD1.6mm, OD1.8mm, OD2.0mm, OD2.2mm, OD2.6mm, OD3.0mm, OD4.5mm, OD5.0mm, OD6.5mm, OD7.0mm, OD8.5mm, OD10.0mm, OD12.0mm, OD15.0mm, OD20.0mm, OD25.0mm, OD30.0mm, OD35.0mm.

Cylinder: OD5mm*Height5mm, OD7*H7, OD10*H10, OD12.7*12.7, OD15*H15, OD20*H20

High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling

High-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling

High-Performance Y-Tzp Zirconia Beads for Precision Ceramic MillingHigh-Performance Y-Tzp Zirconia Beads for Precision Ceramic MillingHigh-Performance Y-Tzp Zirconia Beads for Precision Ceramic MillingHigh-Performance Y-Tzp Zirconia Beads for Precision Ceramic MillingHigh-Performance Y-Tzp Zirconia Beads for Precision Ceramic Milling


 