Premium Partially Stabilized Zirconia Ceramics with Magnesium Oxide

• Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic
• Type: Ceramic Parts
• Size: Customized
• Model NO.: MSZ-6
• Advantage: Long Service Life
• Color: Yellow
• Applicable Industries: Hotels, Garment Shops, Building Material Shops
• Material: Zirconia Ceramic
• Transport Package: Plastic Bag, Wooden Box
• Specification: 0.1mm,0.2mm,0.5mm,1.0mm or according to requiement
• Trademark: yinghua
• Origin: China
• Production Capacity: 500000

Product Description

Magnesium oxide partially stabilized zirconia ceramics (Mg-PSZ or MSZ) have unparalleled advantages in high temperature and high humidity, and can be used for a long time without aging at low temperature. High quality Mg-PSZ ceramics have good moisture resistance, thermal shock resistance, excellent fracture toughness and high temperature mechanical strength, can withstand use temperature up to 800 ºC or higher (up to 2000 ºC), Mg-PSZ ceramics is free from wetting and best corrosion resistance to acid, alkali, liquid glass and molten metal .
 

ITEM		1		2
		Y-TZP		MgO-PSZ
1	(%)	ZrO2	Y2O3	ZrO2	MgO
	Chemical Composition	94.6	5.2	96.5	3.5
2		White		Yellow
	Color
3	(g/cm^3)	6.05		5.70
	Density
4	(%)	0		0
	Water Absorption
5		9		9
	Hardness Mohs
6	(Kg/mm^2)	1300		1100
	Hardness Vickers
7	(Gpa)	200		250
	Young's Modulus
8	(MPa)	1250		450
	Bending Strength
9	(Mpa*M^1/3)	10.0		6.5
	Fracture Toughness
10	(MPa)	3000		2500
	Compressive Strength
11	(10^-6/K)	10.0		10.0
	Expansion Coefficient
12	(W/mK)	3		3
	Thermal Conductivity
13		20.0		28.0
	Dielectric Constant
14	(Ω·Cm)	>10^12		>10^14
	Volume Resistivity