Premium Y-Tzp Psz Zirconia Beads for Ceramic Milling

• Application: Industrial Ceramic
• Type: Ceramic Balls
• Size: OEM
• Model NO.: bead
• Advantage: Long Service Life
• Color: White
• Applicable Industries: Hotels, Garment Shops, Building Material Shops
• Material: Zirconia Ceramic
• Transport Package: Plastic Bag, Wooden Box
• Specification: 0.1MM~50MM
• Trademark: yinghua
• Origin: China

Product Description

1. Introduction:
TZP Milling Media is made from Yttria partially stabilized zirconia, and available for any kinds of mills such as micro mill, ultromicro mill, vibratory mill and ball mill to grind and disperse the material effectively and economically. Characterized with high density and toughness, super hardness, excellent Wear and corrosion resistance, the TZP milling media is regarded as an most attractive material in many applications include: electronic slurry, ceramic powder, magnetic material, battery material, rare-earth material, nonmetal ore, painting, dye, ink, calcium, titanium, pesticide, food stuff and medicine etc. Superior grinding efficiency and minimizing product contamination from media wear are most valued.
2. Main Properties:
Type-1: High Density

Constituents (%)	ZrO2 Y2O3	94.6 5.25
Density	g/cm³	6.05
Open Porosity	%	0
Hardness Vickers	Hv	1250
E modulus	Gpa	200
Bending strength (4-point)	MPa	1300
Fracture strength	MPa*m1/2	8
CTE(20~4000C)	*10-6/ K	9.6

Type-2: Low Density

Constituents (%)	ZrO2 Y2O3	94.6 5.25
Density	g/cm³	5.80
Hardness Vickers	Hv	1100
E modulus	Gpa	200
Bending strength (4-point)	MPa	900
Fracture strength	MPa*m1/2	>6

3. Main Specifications:
Ball: OD0.6mm, OD0.8mm, OD1.0mm, OD1.2mm, OD1.4mm, OD1.6mm, OD1.8mm, OD2.0mm, OD2.2mm, OD2.6mm, OD3.0mm, OD4.5mm, OD5.0mm, OD6.5mm, OD7.0mm, OD8.5mm, OD10.0mm, OD12.0mm, OD15.0mm, OD20.0mm, OD25.0mm, OD30.0mm, OD35.0mm.

Cylinder: OD5mm*Height5mm, OD7*H7, OD10*H10, OD12.7*12.7, OD15*H15, OD20*H20